Experimental investigation of a nano coating efficiency for dust mitigation on photovoltaic panels in harsh climatic conditions

Abstract

Dust accumulation on photovoltaic (PV) panels in arid regions diminishes solar energy absorption and panel efficiency. In this study, the effectiveness of a self-cleaning nano-coating thin film is evaluated in reducing dust accumulation and improving PV Panel efficiency. Surface morphology and elemental analysis of the nano-coating and dust are conducted. Continuous measurements of solar irradiances and ambient temperature have been recorded. SEM analysis of dust revealed irregularly shaped micron-sized particles with potential adhesive properties, causing shading effects on the PV panel surface. Conversely, the coating particles exhibited a uniform, spherical shape, suggesting effective prevention of dust adhesion. Solar irradiance ranged from 120 W/m² to a peak of 720 W/m² at noon. Application of the self-cleaning nano-coating thin film consistently increased short circuit current (I_sc), with the coated panel averaging 2.8 A, which is 64.7% higher than the uncoated panel's 1.7 A. The power output of the coated panel ranged from 7 W to 38 W, with an average of approximately 24.75 W, whereas the uncoated panel exhibited a power output between 3 W and 23 W, averaging around 14 W. These findings highlight the substantial potential of nano-coating for effective dust mitigation, particularly in dusty environments, thus enhancing PV system reliability.