Deep Drawing Behaviour of Steel–Glass Fibre-Reinforced and Non-Reinforced Polyamide–Steel Sandwich Materials

Abstract

Thermoplastic-based fibre metal laminates (FMLs) have gained increasing interest in the automotive industry due to their forming potential—especially at higher temperatures—into complex components compared to thermoset-based ones. However, several challenges arise while processing thermoplastic-based FMLs. One the one hand, forming at room temperature (RT) leads to early failure modes, e.g., fracture and delamination. On the other hand, warm forming can extend their forming limits, although further defects arise, such as severe thickness irregularities and wrinkling problems. Therefore, this study focuses on developing different approaches for deep drawing conditions to deliver a promising, feasible, and cost-effective method for deep-drawn FML parts. We also describe the defects experimentally and numerically via the finite element method (FEM). The FMLs based on steel/glass fibre-reinforced polyamide 6 (GF-PA6/steel) are studied under different deep drawing conditions (temperatures, punch, and die dimensions). In addition, mono-materials and sandwich materials without fibre reinforcement are investigated as benchmarks. The results showed that the best deep drawing condition was at a temperature of 200 °C and a die/punch radius ratio of 0.67, with a gap/thickness ratio of ≤2.0. The FEM simulation via Abaqus 6.14 was able to successfully replicate the anisotropic properties and wrinkling of the GF-PA6 core in an FML, resembling the experimental results.