Adsorption Performance and Mechanistic Pathways of Raw Powdered Pine Cone Toward the Removal of Dye and Cr(VI)

Abstract

ABSTRACT This work aims to valorize pine cones powder (PCP), an agricultural waste, as a bioadsorbent for the removal of a cationic dye, Rhodamine B (RhB), and hexavalent chromium Cr(VI) from an aqueous solution. The adsorbent was characterized by scanning electron microscopy (SEM), Fourier‐transformed infrared (FTIR), and X‐ray diffractometer (XRD) spectroscopy. Adsorption studies were carried out in a batch mode under different operating parameters like initial solution pH (2–11), adsorbent dosage (0.025–0.6 g), initial contaminant concentration (20–100 mg/L), temperature (283–328K), contact time (0–120 min), and ionic strength (NaCl, MgCl 2 , CuSO 4 , Na 2 SO 4 , and FeCl 3 ). The optimum conditions for adsorption for Cr(VI) were; ([Cr(VI)] = 30 mg/L, pH = 2, adsorbent dose = 1.5 g/L, T = 25°C), and for RhB: ([RhB] = 30 mg/L, pH = 4.6, adsorbent dose = 4 g/L, T = 25°C). Under these conditions, the maximum adsorption capacities reached were 19.861 and 6.565 mg/g, for Cr(VI) and RhB, respectively. The inhibiting effect of the studied salts on RhB dye and metal ion removal is as follows: FeCl 3 > CuSO 4 > MgCl 2 > Na 2 SO 4 > NaCl. The Freundlich isotherm described the best the adsorption of Cr (VI) and RhB onto PCP, since it gave the highest R 2 values (R 2 ≥ 0.983) associated with the lowest error values (χ 2 , RMSE, and Δq). The calculated Dubinin–Radushkevich mean energy (E) is less than 8 kJ/mol. It is 3.391 kJ/mol for Cr(VI) and 2.310 kJ/mol for RhB sorption, respectively, confirming the physical character of adsorption onto PCP sorbent. Experimental data for Cr(VI) and RhB ion adsorption onto PCP, fitted well the pseudo‐second‐order kinetic model (R 2 ≥ 0.997). According to the thermodynamic analysis, the retention of Cr(VI) and RhB followed a physisorption, endothermic, and spontaneous process at all temperatures for Cr(VI), and at higher temperatures for RhB dye. These results suggest that raw PCP may be envisaged as a promising biosorbent for water remediation without the need of costly heat and activation processes as a cheap and sustainable adsorption process.